Long-term leaching of photovoltaic modules

Some photovoltaic module technologies use toxic materials. We report long-term leaching on photovoltaic module pieces of 5 × 5 cm 2 size. The pieces are cut out from modules of the four major commercial photovoltaic technologies: crystalline and amorphous silicon, cadmium telluride as well as from copper indium gallium diselenide. To simulate different environmental conditions, leaching occurs at room temperature in three different water-based solutions with pH 3, 7, and 11. No agitation is performed to simulate more representative field conditions. After 360 days, about 1.4% of lead from crystalline silicon module pieces and 62% of cadmium from cadmium telluride module pieces are leached out in acidic solutions. The leaching depends heavily on the pH and the redox potential of the aqueous solutions and it increases with time. The leaching behavior is predictable by thermodynamic stability considerations. These predictions are in good agreement with the experimental results.