Intergranular Corrosion Behaviour of a New Austenitic Stainless Steel Low in Nickel

A comparative study was done on the intergranular corrosion resistance of AISI 304 stainless steel and a new austenitic stainless steel currently being developed, in which the concentration of nickel is less than 2%. The austenitic effect of nickel is replaced by other alloying elements, mainly manganese. The experimental results are discussed according to ASTM A-262, practices C and E (Huey and modified Strauss). A study of both materials under several test conditions was carried out using scanning electron microscopy to analyze the microstructural characteristics and the attack morphology. Résumé Nous avons fait une étude comparative de la résistance à la corrosion intergranulaire d'un acier inoxydable AISI 304 et d'un nouvel acier austénitique inoxydable en cours de développement dont la teneur en nickel est inférieure à 2%. L'effet austénitique du nickel est remplacé par d'autres éléments de l'alliage, principalement du manganèse. Nous parlons des résultats expérimentaux en accord avec les procédures C et E (Huey et Strauss modifié) de la norme ASTM A-262. Une étude des deux matériaux soumis à plusieurs conditions de tests, au moyen d'un microscope à balayage électronique (SEM), pour analyser les caractéristiques microstructurelles et la morphologie d'attaque est effectuée.