Confinement-Enhanced Rapid Interlayer Diffusion within Graphene-Supported Anisotropic ReSe₂ Electrodes

To enhance interlayer lithium diffusion, we engineer electrodes consisting of epitaxially grown ReSe 2 nanosheets by chemical vapor deposition, supported on three-dimensional (3D) graphene foam, taking advantage of its weak van der Waals coupling and anisotropic crystal structure. We further demonstrate its excellent performance as the anode for lithium-ion battery and catalyst for hydrogen evolution reaction (HER). Density functional theory calculation reveals that ReSe 2 exhibits a low energy barrier for lithium (Li) interlayer diffusion because of negligible interlayer coupling and anisotropic structure with low symmetry that creates additional adsorption sites and leads to a reduced diffusion barrier. Benefitting from these properties, the 3D ReSe 2 /graphene foam electrode displays excellent cycling and rate performance with 99.6% capacity retention after 350 cycles and a capacity of 327 mA h g –1 at the current density of 1000 mA g –1 . Additionally, it has exhibited a high activity for HER, in which an exchange current density of 277.8 μA cm –2 is obtained and only an overpotential of 106 mV is required to achieve a current density of −10 mA cm –2 . Our work provides a fundamental understanding of the interlayer diffusion of Li in transition-metal dichalcogenide (TMD) materials and acts as a new tool for designing a TMD-based catalyst.