Estimate of the Activation Energies for Boundary Diffusion from Rate‐Controlled Sintering of Pure Alumina, and Alumina Doped with Zirconia or Titania

Sintering experiments at constant heating rates were employed to estimate the activation energy for sintering in alumina and in alumina containing 5 vol% zirconia or 5 vol% titania. Grain growth, which can complicate the analysis of sintering kinetics data, was suppressed by using uniformly and densely packed grain compacts prepared by colloidal processing. Grain‐boundary diffusion is believed to have been the dominant sintering mechanism. The activation energies were 440 ± 40 kJ/mol for pure alumina, 585 ± 40 kJ/mol for alumina (titania), and 730 ± 60 kJ/mol for alumina (zirconia). The alumina and alumina (titania) results are in agreement with the values reported in the literature. The possibility that the higher activation energies for doped alumina reflect a stronger bonding at alumina interfaces in the presence of zirconium and titanium is discussed.