Novel polyether polyurethane/clay nanocomposites synthesized with organicly modified montmorillonite as chain extenders

A kind of novel polyether polyurethane (PU)/clay nanocomposite was synthesized using poly(tetramethylene glycol), 4,4′‐diphenylmethane diisocyanate (MDI), 1,6‐hexamethylenediamine, and modified Na + ‐montmorillonite (MMT). Here, organicly modified MMT (O‐MMT) was formed by applying 1,6‐hexamethylenediamine as a swelling agent to treat the Na + ‐MMT. The X‐ray analysis showed that exfoliation occurred for the higher O‐MMT content (40 wt %) in the polymer matrix. The mechanical analysis indicated that, when the O‐MMT was used as a chain extender to replace a part of the 1,2‐diaminopropane to form PU/clay nanocomposites, the strength and strain at break of the polymer was enhanced when increasing the content of O‐MMT in the matrix. When the O‐MMT content reached about 5%, the tensile strength and elongation at break were over 2 times that of the pure PU. The thermal stability and the glass transition of the O‐MMT/PU nanocomposites also increased with increasing O‐MMT content.