Abstract The fabrication of high‐quality perovskite film highly relies on chemical composition and the synthesis method of perovskite. So far, sequentially deposited MA 0.03 FA 0.97 Pb(I 0.97 Br 0.03 ) 3 polycrystalline film is adopted to produce high‐performance perovskite solar cells with record power conversion efficiency (PCE). Fewer grain boundaries and incorporation of inorganic cation (e.g., cesium) would further increase device performance via sequential deposition. Here, cesium chloride (CsCl) is introduced into lead iodide (PbI 2 ) precursor solution that beneficially modulates the property of PbI 2 film, leading to larger grains with cesium incorporation in the resulting perovskite film. The enlarged crystal grains originate from a slower nucleation process for CsCl‐containing PbI 2 film when reacting with formamidine iodide, confirmed by in situ confocal photoluminescence imaging. Photovoltaic devices based on CsCl‐containing PbI 2 film demonstrate a higher averaging efficiency of 21.3% than 20.3% of the devices without CsCl additives for reverse scan. More importantly, the device stability is improved by CsCl additives that retain over 90% of their initial PCE value after 4000 min tracking at maximum power point under 1‐sun illumination. This work paves a way to further improve the photovoltaic performance of mixed‐cation‐halide perovskite solar cells via a sequential deposition method.
Li et al. (Thu,) studied this question.