AlFe2–xCoxB₂ (x = 0–0.30): TC Tuning through Co Substitution for a Promising Magnetocaloric Material Realized by Spark Plasma Sintering

AlFe 2 B 2 and AlFe 2– x Co x B 2 ( x = 0–0.30) were synthesized from the elements in three different ways. The samples were characterized by powder X-ray diffraction, Rietveld refinements, energy-dispersive X-ray spectroscopy, and magnetic measurements. Using Al flux the formation of AlFe 2 B 2 single crystals is preferred. Arc melting enables the substitution of ∼6% Co. This substitution of Fe by Co decreases the Curie temperature T C from 290 to 240 K. The highest Co substitution up to 15% is achieved by spark plasma sintering (SPS). T C is reduced to 205 K. In all cases an excess of Al is necessary to avoid the formation of ferromagnetic FeB. Al 13 Fe 4– x Co x is the common byproduct. T C and the cobalt content are linearly correlated. The transition paramagnetic–ferromagnetic remains sharp for all examples. The magnetic entropy change of the Co-containing samples is comparable to AlFe 2 B 2 . SPS synthesis yields, in short reaction times, a homogeneous and dense material with small amounts of paramagnetic Al 13 Fe 4–x Co x as an impurity, which can serve as sinter additive. These properties make AlFe 2– x Co x B 2 a promising magnetocaloric material for applications between room temperature and 200 K.