A very large magnetic entropy change ΔS has been observed in Fe-based cubic NaZn13-type compound LaFe11.2Co0.7Si1.1 near the Curie temperature TC of 274 K. The value of the entropy change is ∼20.3 J/kg K under a magnetic field of 5 T at TC=274 K. It markedly exceeds that of pure Gd at the corresponding temperature range [V. K. Pecharsky & K. A. Gschneidner, Jr., Phys. Rev. Lett. 78, 4494 (1999)]. The great entropy change produced by the sharp change of magnetization is associated with a large negative lattice expansion at TC. The very large magnetic entropy change and low cost suggest that the compound LaFe11.2Co0.7Si1.1 has great potential for applications as magnetic refrigerants near room temperature.