Modifications of single-wall carbon nanotubes upon oxidative purification treatments

A systematic characterization of single-wall carbon nanotube (SWCNT) material after successive purification steps, including reflux treatment with nitric acid, air oxidation, and annealing, has been performed. Inductively coupled plasma–optical emission spectroscopy shows that a considerable reduction of the metal impurities by up to 95% can be obtained by the nitric acid reflux treatment. During this process, Raman spectroscopy clearly proves that HNO 3 molecules are intercalated into the bundles of SWCNTs. At the same time, SWCNTs have suffered a high degree of degradation and defects are being introduced. The subsequent thermal processes lead to the removal of further defect carbon materials and to the almost complete de-intercalation of the HNO 3 molecules. Transmission electron microscopy reveals that the remaining SWCNT bundles tend to form thick bundles. Thus the applied purification process results in a high-purity SWCNT material with a drastically reduced content of metal nanoparticles and composed of large bundles of SWCNTs.