Nanoporous Gold-Based Biofuel Cells on Contact Lenses

A lactate/O 2 enzymatic biofuel cell (EBFC) was prepared as a potential power source for wearable microelectronic devices. Mechanically stable and flexible nanoporous gold (NPG) electrodes were prepared using an electrochemical dealloying method consisting of a pre-anodization process and a subsequent electrochemical cleaning step. Bioanodes were prepared by the electrodeposition of an Os polymer and Pediococcus sp . lactate oxidase onto the NPG electrode. The electrocatalytic response to lactate could be tuned by adjusting the deposition time. Bilirubin oxidase from Myrothecium verrucaria was covalently attached to a diazonium-modified NPG surface. A flexible EBFC was prepared by placing the electrodes between two commercially available contact lenses to avoid direct contact with the eye. When tested in air-equilibrated artificial tear solutions (3 mM lactate), a maximum power density of 1.7 ± 0.1 μW cm –2 and an open-circuit voltage of 380 ± 28 mV were obtained, values slightly lower than those obtained in phosphate buffer solution (2.4 ± 0.2 μW cm –2 and 455 ± 21 mV, respectively). The decrease was mainly attributed to interference from ascorbate. After 5.5 h of operation, the EBFC retained 20% of the initial power output.