Deep sub-micron stud-via technology of superconductor VLSI circuits

A fabrication process has been developed for fully planarized Nb-based superconducting interlayer connections (vias) with minimum size down to 250 nm for superconductor very large scale integrated (VLSI) circuits with 8 and 10 superconducting layers on 200-mm wafers. Instead of etched contact holes in the interlayer dielectric it employs etched and planarized Nb pillars (studs) as connectors between adjacent wiring layers. Detailed results are presented for one version of the process that utilizes Nb/Al/Nb trilayers for each wiring layer instead of single Nb wiring layers. Nb studs are etched in the top layer of the trilayer to provide vertical connections between the wires etched in the bottom layer of the trilayer and the next wiring layer that is also deposited as a Nb/Al/Nb trilayer. This technology makes possible a dramatic increase in the density of superconducting digital circuits by reducing the area of interconnects with respect to presently utilized etched contact holes between superconducting layers and by enabling the use of stacked vias. Results on the fabrication and size dependence of electric properties of Nb studs with dimensions near the resolution limit of 248-nm photolithography are presented in the normal and superconducting states. Superconducting critical current density in the fabricated stud-vias is about 0.3 A μm −2 and approaches the depairing current density of Nb films.