Quantification of Sensitization in AA5083-H131 via Imaging Ga-Embrittled Fracture Surfaces

Sensitization of 5xxx series Al alloys involving precipitation of β phase (Mg2Al3) at grain boundaries was studied for different exposure times at 100°C upon AA5083-H131 (UNS A95083). In this work, we reveal that fracture surfaces prepared by liquid gallium embrittlement can yield a quantification of grain boundary β phase with significant statistics on β phase size and spacing. This information is a necessary first step toward development of quantitative damage models to describe inter-granular corrosion (IGC) and stress corrosion (IGSCC).