Carbon-Doped TiO₂ and Carbon, Tungsten-Codoped TiO₂ through Sol–Gel Processes in the Presence of Melamine Borate: Reflections through Photocatalysis

A series of C-doped, W-doped, and C,W-codoped TiO 2 samples have been prepared using modified sol–gel techniques. Reproducible inexpensive C-doping arises from the presence of melamine borate in a sol–gel mixture, whereas W-doping is from the addition of tungstic acid to the sol. The materials have been characterized using elemental analysis, N 2 physisorption (BET), thermogravimetric analysis, X-ray diffraction, Raman, X-ray photoelectron, UV–vis spectroscopies, and photocatalytic activity measurements. Doping C and W independently results in an increased absorbance in the visible region of the spectrum with a synergistic effect in increased absorbance when both elements are codoped. The increased visible-light absorbance of the W-doped or codoped materials is not reflected in photocatalytic activity. Visible-light-induced photocatalytic activity of C-doped material was superior to that of an undoped catalyst, paving the way for its application under only visible-light irradiation conditions. A significant fraction of the spectral red shift commonly observed with doped catalysts might be due to the formation of color centers as a result of defects associated with oxygen vacancies, and bandgap-related narrowing or intragap localization of dopant levels are not the only factors responsible for enhanced visible-light absorption in doped photocatalysts. Furthermore, bandgap narrowing through increases in the energy of the valence band may actually decrease photo-oxidation activity through a curtailment of one route of oxidation.