Broad-Band Antireflection Coating at Near-Infrared Wavelengths by a Breath Figure

We prepared a porous thin film by spin-coating of a cellulose acetate butyrate (CAB) solution in tetrahydrofuran under a humid environment. Due to evaporative cooling during spin-coating, condensed water droplets were formed by a breath figure on the CAB solution, and these developed a porous structure after complete drying. By varying the solution concentration and rotating speeds, two distinct morphologies were generated: top and bottom layers with higher and lower porosities, respectively. We found that the two-layer porous film coated on glass exhibited low reflectance of less than 1% in the near-infrared (NIR) regime corresponding to wavelengths between 900 and 2200 nm. Since the porous structure was very uniform over a large area, the film could be easily employed for broad-band antireflection coating at NIR wavelengths.