p-type conductivity in wide-band-gap BaCuQF (Q=S,Se)

BaCuQF (Q=S,Se) materials, candidate transparent p-type conductors, were prepared by solid-state reaction, and their bulk electrical and optical properties were evaluated. The room-temperature Seebeck coefficient and electrical conductivity of undoped BaCuQF pellets were +56 μV/K and 0.088 S/cm, respectively, for the sulfide fluoride, and +32 μV/K and 0.061 S/cm, respectively, for the selenide fluoride. The conductivity was greatly enhanced by the substitution of several percent of K for Ba; the highest conductivities were 82 S/cm for Ba0.9K0.1CuSF and 43 S/cm for Ba0.9K0.1SeF. The band gaps for Q=S and Q=Se were measured to be 3.2 and 3.0 eV, respectively. Undoped BaCuSF exhibits strong red luminescence near 630 nm under ultraviolet excitation.