Chitosan–ammonium acetate–ethylene carbonate membrane for proton batteries

Proton-conducting membranes were prepared using a solution-casting technique. The highest membrane conductivity of (3.83 ± 0.73) × 10−3 S cm−1 was achieved in chitosan acetate–50 wt.% ammonium acetate–70 wt.% ethylene carbonate. The batteries were fabricated with a configuration of Zn + ZnSO4·7H2O ‖ chitosan membrane ‖ MnO2 and Zn + ZnSO4·7H2O ‖ chitosan membrane ‖ V2O5. The cathode materials produced open circuit voltages of 1.60 and 1.27 V using manganese (IV) oxide (MnO2) and vanadium (IV) oxide (V2O5), respectively. The discharge capacities of the batteries were 45.0 and 34.7 mA h using MnO2 and V2O5 cathode at 1.0 mA, respectively. The maximum power densities were 1.83 mW cm−2 for the battery with MnO2 and 1.36 mW cm−2 for the battery with V2O5 cathode.