Materials characterization study reveals efficient energy transfer and low resistivity in terbium-ytterbium co-doped zinc oxide films, highlighting potential for photovoltaic devices.
Structural, optical and electrical properties of (ytterbium/terbium) co-doped ZnO thin films deposited on glass substrates using the spray pyrolysis method were investigated. The films exhibited the hexagonal wurtzite structure with a preferential orientation along (002) direction. No secondary phase was observed in the X-ray diffraction detection limit. Atomic force microscopy (AFM) was performed and root means square roughness (RMS) of our samples decreased with terbium content. Photoluminescence measurements showed a luminescence band at 980 nm which is characteristic of Yb3+ transition between the electronic levels 2F5/2 to 2F7/2. This is experimental evidence for an efficient energy transfer from the ZnO matrix to Yb. Hall Effect measurements gave a low electrical resistivity value around 6.0 × 10−3 Ω.cm. Such characteristics make these films of interest to photovoltaic devices.
No takes yet. Share an insight, caveat, or question.
hat et al. (2020) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: