Ionic conductivity of hybrid films based on polyacrylonitrile and their battery application

The alternate current (AC) and direct current (DC) ionic conductivity of hybrid films composed of polyacrylonitrile (PAN), lithium perchlorate (LiClO 4 ), and a plasticizer was studied. Three kinds of the plasticizer [ethylene carbonate (EC), propylene carbonate (PC), N , N ‐dimethylformamide (DMF)] were used. Suitability of these hybrid films for lithium battery was investigated. The AC conductivity, which represents bulk ionic conductivity, was dependent on the component and the composition of the hybrid films, ranging from 10 −4 −10 −8 Scm −1 . The AC conductivity was mainly determined by the molar ratio of [plasticizer]/[LiClO 4 ] in the hybrid films and increased with the increase in this ratio. The effect of the plasticizer on the enhancement in the AC conductivity was in the following order. DMF>EC>PC. The hybrid films with both electrodes of lithium showed the stable DC conductivity of about 1/10 of the AC conductivity, except for the hybrid films containing DMF. The hybrid films were found to be effective as a lithium ionic conductor. The galvanic cell. Li/sample/MnO 2 , at the discharge current density of 90 μA/cm 2 showed the stable electromotive force of about 3 V for 70 h.