Hierarchical Tubular Structures Composed of Co₃O₄ Hollow Nanoparticles and Carbon Nanotubes for Lithium Storage

Hierarchical tubular structures composed of Co3 O4 hollow nanoparticles and carbon nanotubes (CNTs) have been synthesized by an efficient multi-step route. Starting from polymer-cobalt acetate (Co(Ac)2 ) composite nanofibers, uniform polymer-Co(Ac)2 @zeolitic imidazolate framework-67 (ZIF-67) core-shell nanofibers are first synthesized via partial phase transformation with 2-methylimidazole in ethanol. After the selective dissolution of polymer-Co(Ac)2 cores, the resulting ZIF-67 tubular structures can be converted into hierarchical CNTs/Co-carbon hybrids by annealing in Ar/H2 atmosphere. Finally, the hierarchical CNT/Co3 O4 microtubes are obtained by a subsequent thermal treatment in air. Impressively, the as-prepared nanocomposite delivers a high reversible capacity of 1281 mAh g(-1) at 0.1 A g(-1) with exceptional rate capability and long cycle life over 200 cycles as an anode material for lithium-ion batteries.