The thermal behavior of various cellulose samples with different degrees of crystallinity as measured by X‐ray diffraction techniques was studied with a differential scanning calorimeter (DSC). The broad endothermic peak which appears between 110 and 160°C is due to loss of absorbed (bound) water. Since a direct relationship was observed between the area of this peak and the crystallinity of the sample, a new procedure for estimating cellulose accessibility (which is related to crystallinity) was proposed and developed. DSC curves obtained on cellulose samples preconditioned at certain constant relative humidities were used to determine sample accessibilities by the proposed method. The accessibility values obtained by DSC showed excellent agreement with crystallinity values determined by more traditional techniques. Completely amorphous cellulose was obtained by anhydrous deacetylation of cellulose triacetate and was used as the standard amorphous cellulose material.
No takes yet. Share an insight, caveat, or question.
Bertran et al. (1986) studied this question.
Synapse has enriched 4 closely related papers on similar clinical questions. Consider them for comparative context: