Some Properties of Polyelectrolyte-G rafted Cellulose

Anionic and cationic polyelectrolytes were grafted on a bleached kraft pulp. Grafting an anionic polyelectrolyte (sodium poly-acrylate-polyacrylamide copolymer) resulted in modified fibers possessing outstanding affinity for water and saline solutions in the pH range where the polymer is ionized. Swelling is the result of both the grafting operation itself and of the presence of the ionized polyelectrolyte. The swollen grafted fibers could be disintegrated under intense shear to give a colloidal solution exhibiting pseudoplastic thixo-tropic behavior. Electron microscopic examination revealed that during the shearing process the fiber had been disintegrated into its constitutive elements, long rodlike protofibrils, which are believed to be mainly responsible for the high viscosities observed. Grafting a cationic polyelectrolyte (polydimethylamino ethyl methacrylate hydrochloride) produced fibers with lower but significant water swelling. The influence of pH on swelling was similar, although reversed, to that observed with the anionic grafted fibers. The presence of a large number of cationic groups in the porous cellulose fiber gel points to applications in ion-exchange and adsorption processes.