Copper-zeolites Prepared by Solid-state Ion Exchange - Characterization and Evaluation for the Direct Conversion of Methane to Methanol

This is the authors' abstract. We don't add key points for this paper.

Direct conversion of methane to methanol (MTM) over Cu-zeolites is a so-called “dream reaction” for the chemical industry. There is still a lot that can be done in order to optimize the reaction by e.g. achieving a deeper understanding of the reaction mechanism and the nature of the Cu-sites. In this study, we investigated a solid-state ion exchange method to incorporate Cu I ions into zeolites (MOR, BEA, ZSM-5 and FAU), as a more scalable technique. The solid-state ion exchange led to a Cu/Al ration of about 0.8, however with a heterogeneous distribution of Cu. Regardless, Fourier transform-infrared spectroscopy still revealed that most Brønsted acid sites were exchanged in all four samples. Further, CH 4 -temperature programmed reaction experiments showed that some Cu-sites formed were reactive towards CH 4 , with Cu I -MOR and Cu I -FAU having the largest CH 4 consumption. Ultimately, the Cu I -zeolites were tested in the MTM reaction and proved capable of producing methanol, even without the presence of Brønsted sites. A MOR with lower Cu/Al ratio (0.30) was also tested for comparison, and as this sample obtained a much higher productivity than the Cu I -MOR with high Cu-loading (0.10 vs. 0.03 mol MeOH /mol Cu ), it was demonstrated that some fine-tuning is necessary to obtain the active Cu sites for methane activation.