Relaxor-ferroelectric superlattices: high energy density capacitors

We report the breakdown electric field and energy density of laser ablated BaTiO(3)/Ba((1-x))Sr(x)TiO(3) (x = 0.7) (BT/BST) relaxor-ferroelectric superlattices (SLs) grown on (100) MgO single crystal substrates. The dielectric constant shows a frequency dispersion below the dielectric maximum temperature (T(m)) with a merger above T(m) behaving similarly to relaxors. It also follows the basic criteria of relaxor ferroelectrics such as low dielectric loss over wide temperature and frequency, and 50 K shift in T(m) with change in probe frequency; the loss peaks follow a similar trend to the dielectric constant except that they increase with increase in frequency (~40 kHz), and satisfy the nonlinear Vogel-Fulcher relation. Well-saturated ferroelectric hysteresis and 50-80% dielectric saturation are observed under high electric field (~1.65 MV cm(-1)). The superlattices demonstrate an 'in-built' field in as grown samples at low probe frequency (<1 kHz), whereas it becomes more symmetric and centered with increase in the probe frequency system (>1 kHz) which rules out the effect of any space charge and interfacial polarization. The P-E loops show around 12.24 J cm(-3) energy density within the experimental limit, but extrapolation of this data suggests that the potential energy density could reach 46 J cm(-3). The current density versus applied electric field indicates an exceptionally high breakdown field (5.8-6.0 MV cm(-1)) and low current density (~10-25 mA cm(-2)) near the breakdown voltage. The current-voltage characteristics reveal that the space charge limited conduction mechanism prevails at very high voltage.