The polarization dependence of 1.5µm wavelength GaInAsP/InP quantum-wire structures fabricated by electron beam lithography and two-step organometallic vapor phase epitaxy growth were measured and compared with quantum-film structures fabricated on the same wafer. As a result, clear anisotropic photoluminescence (PL) properties of the quantum-wire structure corresponding to the wire width (25 nm and 35 nm) were confirmed. This anisotropy was observed to be slightly stronger in the 1% compressively-strained quantum-wire structure than that in the lattice-matched one with the same wire width (35 nm).