Miscibility, Thermal Properties, and Enzymatic Degradability of Binary Blends of Poly[(R)-3-hydroxybutyric acid] with Poly(ε-caprolactone-co-lactide)

The miscibility, morphology, and biodegradability of binary blends of poly[( R )-3-hydroxybutyric acid] (P[( R )-3HB]) ( M n = 300 000) with poly(ε-caprolactone- co -lactide) (P(CL- co -LA)) ( M n = 1500−40 000) have been studied by means of differential scanning calorimetry (DSC), optical microscopy, scanning electron microscopy (SEM), enzymatic hydrolysis, and biodegradation in river water. Copolymers of ε-caprolactone (CL) and ( R,S )-lactide (LA) with a wide range of compositions were prepared by ring-opening copolymerization of ε-caprolactone with ( R,S )-lactide in the presence of aluminum triisopropoxide as an initiator. The P(CL- co -LA) samples were found to have a random sequence distribution of monomer units by 13 C NMR analysis. The P(CL- co -LA) films were hydrolyzed by a lipase from Rhizopus delemar, and the rates of enzymatic hydrolysis were higher than that of PCL homopolymer. DSC analysis revealed that the solid-state structure of P[( R )-3HB]/P(CL- co -LA) blends was strongly dependent on the copolymer composition of the P(CL- co -LA) component. The miscible blends of P[( R )-3HB] were prepared with amorphous P(CL- co -LA) ranging from 30 to 100 mol % LA. The spherulites of P[( R )-3HB] in the miscible P[( R )-3HB]/P(CL- co -LA) blends were volume-filled, and the spherulitic growth rate decreased with an increase in the content of the P(CL- co -LA) component. The enzymatic hydrolysis of P[( R )-3HB]/P(CL- co -LA) blend films was carried out at 37 °C and pH 7.4 in a potassium phosphate buffer with an extracellular PHB depolymerase from Alcaligenes faecalis . The rates of enzymatic hydrolysis on the films of P[( R )-3HB]/P(CL- co -LA) blends decreased with an increase in the P(CL- co -LA) content.