Thermophysical and structural properties of manganese ferrite nanoparticles

This paper discusses the results of the research carried out to study the structure, optical properties and thermophysical properties of a sample (nanopowder with a true density of 4.96 g/cm 3 , a particle size of 60 nm and a purity of 98.5%, SkySpring Nanomaterials, USA) with high purity. Based on the results of X-ray diffraction, the crystalline phase of MnFe 2 O 4 ferrite nanoparticles was completely obtained and the values of the lattice parameters were determined. The results of the MID-IR analysis showed that the absorption coefficient [Formula: see text] reaches its maximum value at 748 cm[Formula: see text] wave number. The optical properties of the as-prepared nanostructures were also investigated by VERTEX 70 V diffuse reflectance spectroscopy (DRS). As can be seen from the results of the DSC analysis, the effects occurring in the temperature range up to [Formula: see text]C clearly reflect the nature of the phase transitions and the amount of energy generated in the ferrite samples.