Influence of Mo or Cu doping in Fe/MgO catalyst for synthesis of single-walled carbon nanotubes by catalytic chemical vapor deposition of methane

A series of mono-, bi- or tri-metallic Fe–Mo-Cu/MgO catalysts with the same metal loading of 6 wt% were prepared by impregnation method and used as catalysts for synthesis single-walled carbon nanotubes (SWCNTs) via methane decomposition. XRD, H2-TPR, and nitrogen physisorption techniques were used to characterize the freshly calcined catalysts, while HRTEM, Raman spectroscopy and TGA were employed to investigate the morphology and microstructure of the SWCNTs product. The obtained results indicated that the introduction of Mo or Cu in the Fe/MgO catalyst enhanced the catalytic growth activity. TEM images showed that both bundles and isolated SWCNTs were obtained over Mo containing catalysts, whereas only SWCNTs bundles were grown over the Fe-Cu/MgO catalyst. The obtained SWCNTs having a diameter of around 0.9–2.4 nm. Raman analysis illustrated that all promoted catalysts produced high quality of SWCNTs compared to the unpromoted Fe/MgO catalyst.