A General, Efficient Method of Incorporation of Metal Ions into Ultrathin TiO₂ Films

A general, efficient method was developed to incorporate a variety of second metal ions into ultrathin TiO 2 films. The thin films were first prepared by the surface sol−gel process from a mixture of the matrix-forming titanium alkoxide and template magnesium alkoxide. Mg 2+ ion was removed by acid/base treatment, forming highly efficient and robust ion-exchange sites. A large variety of metal ions, including alkaline, alkaline earth, transition, and rare earth elements, were then incorporated into the thin films by ion exchange with Na + . The amount of incorporation increased with increasing charge of the metal ions. The rate of the ion-exchange process was investigated in the case of Gd 3+ . The incorporated metal ions were immobilized by thermal treatment at 450 °C. The UV absorption edge of the TiO 2 film was extended to the visible region by Fe 3+ doping and calcination.