Mn modified rhombohedral Pb(In0.5Nb0.5)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (PIN-PMN-PT:Mn) single crystals poled along [011]C crystallographic direction exhibit a “2R” engineered domain configuration, with macroscopic mm2 symmetry. The complete sets of material constants were determined using combined resonance and ultrasonic methods, and compared to [001]C poled PIN-PMN-PT:Mn crystals. The thickness shear piezoelectric coefficient d15 and electromechanical coupling factor k15 were found to be on the order of ∼3000 pC/N and 0.92, respectively, with longitudinal piezoelectric coefficient d33 and coupling factor k33 being on the order of ∼1050 pC/N and 0.90. Of particular importance is that PIN-PMN-PT:Mn single crystals exhibited high mechanical quality factor Q33 ∼ 1000, comparable to “hard” PZT8 ceramics, which can also be confirmed by the low extrinsic contribution, being ≤2% from the Rayleigh analysis.
No takes yet. Share an insight, caveat, or question.
Huo et al. (2013) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: