High‐temperature resistance water‐soluble copolymer derived from acrylamide, DMDAAC, and functionalized sulfonamide for potential application in enhance oil recovery

A water‐soluble poly(AM‐AA‐DMDAAC‐TCAP) was prepared using acrylamide (AM), acrylic acid (AA), diallyl dimethyl ammonium chloride (DMDAAC), and N ‐allyl‐4‐methylbenzenesulfonamide (TCAP), and the synthesis conditions were investigated. The obtained copolymer was characterized by FTIR, 1 H‐NMR, SEM, TG, and XRD. The temperature resistance and thickening function of the copolymer are improved significantly compared with that of partially hydrolyzed polyacrylamide. It is found that the viscosity of copolymer could achieve up to 53.3% retention rate at 120°C compared to that at 30°C. About 16.6% for enhanced oil recovery is obtained by poly(AM‐AA‐DMDAAC‐TCAP) brine solution at 65°C. In addition, the results of XRD show that 3000 mg/L copolymer combined with 10 wt % KCl solution could reduce the d‐ spacing of sodium montmorillonite from 18.94 to 14.86 Å exhibiting remarkable effect on inhibiting hydration of clays. All the results demonstrate that poly(AM‐AA‐DMDAAC‐TCAP) have excellent performance for potential application in enhance oil recovery.