GaAs MOSFET Using InAlP Native Oxide as Gate Dielectric

GaAs metal-oxide-semiconductor field-effect transistors (MOSFETs) using wet thermally oxidized InAlP as the gate insulator are reported for the first time. Leakage current measurements show that the 11-nm-thick native oxide grown from an In/sub 0.49/Al/sub 0.51/P layer lattice-matched to GaAs has good insulating properties, with a measured leakage current density of 1.39×10/sup -7/ mA/μm2at 1 V bias. GaAs MOSFETs with InAlP native gate oxide have been fabricated with gate lengths from 7 to 2 μm. Devices with 2-μm-long gates exhibit a peak extrinsic transconductance of 24.2 mS/mm, an intrinsic transconductance of 63.8 mS/mm, a threshold voltage of 0.15 V, and an off-state gate-drain breakdown voltage of 21.2 V. Numerical Poisson's equation solutions provide close agreement with the measured sheet resistance and threshold voltage.