Structure and properties of blend membranes prepared from cellulose and alginate in NaOH/urea aqueous solution

Regenerated cellulose (RC)/alginic acid (AL) blend membranes were satisfactorily prepared from 6 wt % NaOH/4 wt % urea aqueous solution by coagulating with 5 wt % CaCl2 aqueous solution, and then treated with 3 wt % HCl. Morphology, crystallinity, mechanical properties, and thermal stability of the membranes were investigated by scanning electron microscopy (SEM), IR and UV spectroscopes, X-ray diffraction, tensile tests, and thermogravimetric analysis (TGA). The RC/AL blends were miscible in all weight ratios of cellulose to alginate. The membranes have homogeneous mesh structures, and the mesh sizes of the blend membranes (200–2000 nm) significantly increased with increasing alginate content. The crystalline state of the AL membrane prepared from 6 wt % NaOH/4 wt % urea aqueous solution was broken completely, and the crystallinity of the blend membranes decreased with an increase of AL. Comparing with AL membranes, the tensile strength and breaking elongation of the blend membranes were obviously improved in dry and wet states. Therefore, the RC/AL blends offer a promising way of alginate as separate and functional materials used in the wet state.