Sputter-deposited Mg–Al–O thin films: linking molecular dynamics simulations to experiments

Using a molecular dynamics model the crystallinity of Mg x Al y O z thin films with a variation in the stoichiometry of the thin film is studied at operating conditions similar to the experimental operating conditions of a dual magnetron sputter deposition system. The films are deposited on a crystalline or amorphous substrate. The Mg metal content in the film ranged from 100% (i.e. MgO film) to 0% (i.e. Al 2 O 3 film). The radial distribution function and density of the films are calculated. The results are compared with x-ray diffraction and transmission electron microscopy analyses of experimentally deposited thin films by the dual magnetron reactive sputtering process. Both simulation and experimental results show that the structure of the Mg–Al–O film varies from crystalline to amorphous when the Mg concentration decreases. It seems that the crystalline Mg–Al–O films have a MgO structure with Al atoms in between.