Polymerization of methyl methacrylate under ultrasonic irradiation. Part IV. Effect of ultrasonic irradiation on Grignard catalyst and stereoregularity of the polymers produced in dioxane–tetrahydrofuran mixed solvent

Two series of polymerization of methyl methacrylate with Grignard reagent in dioxane—tetrahydrofuran mixed solvent was carried out under ultrasonic irradiation. In series A, catalyst was added to the mixture of monomer and solvent, and in series B, catalyst was previously mixed with solvent. The effect of ultrasonic irradiation on Grignard catalyst and the microstructure in reacting sites were discussed on the basis of the stereoregularity of the polymers produced. The stereoregularity of the polymers in series A was higher than that in series B. The effect of ultrasonic irradiation on the stereoregularity was completely reversed in series A and B and it increased in the former and decreased in the latter. It was, therefore, assumed that ultrasonic irradiation affected the microstructure in the reacting sites in series A, while it increased the relative amount of R 2 Mg which gave polymers with poor stereoregularity in series B.