LiTi2(PO4)3-lithium salt systems have been investigated in order to obtain a high lithium ion conductor. The salts acted as binder for sintering. The porosity decreased considerably and the conductivity of the pellets increased by the binder utilization. The maximum conductivity was 3 × 10−4 S·cm−1 for the LiTi2(PO4)3–0.2Li3BO3 system. The mixed binder was found to exist as a glassy or a thin coating second phase.