Crystal structure and morphology of phenyl‐capped tetraaniline in the leucoemeraldine oxidation state

A series of crystals of phenyl‐capped tetraaniline in the leucoemeraldine oxidation state were obtained at different isothermal temperatures and were observed directly under transmission electron microscope. The crystals obtained at higher temperatures exhibit more perfect structures than those obtained at lower temperatures. Both the lamella thickness and the crystal size increase with crystallization temperature. The tetraaniline is apt to form larger scale crystals under lower degree of supercooling. However, their crystal structures keep steady with the crystallization temperature. The tetramer was found to adopt a monoclinic lattice with unit cell parameter of a = 13.93 Å, b = 8.82 Å, c = 23.20 Å, and β = 95.03°, as determined using electron diffraction tilting method combined with wide‐angle X‐ray diffraction experiment.