High performance dye-sensitized solar cell based on 2-mercaptobenzimidazole doped poly(vinylidinefluoride-co-hexafluoropropylene) based polymer electrolyte

In this work, the influence of 2-mercaptobenzimidazole (2-MCBI) on poly(vinylidinefluoride-co-hexafluoropropylene)/KI/I2 (PVDF-HFP/KI/I2) polymer electrolytes were studied. The pure and different weight percentage ratios (20, 30, 40 and 50%) of 2-MCBI doped PVDF-HFP/KI/I2 electrolytes were prepared by a solution casting technique. The as-prepared polymer electrolyte films were characterized using various techniques such as Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC), X-ray diffractometer (XRD), alternating current (AC)-impedance analysis. The addition of 2-MCBI with pure PVDF-HFP/KI/I2 was found to increase the ionic conductivity of electrolyte. Among the various additions, 30 wt% 2-MCBI doped PVDF-HFP/KI/I2 showed the highest room temperature ionic conductivity values than the others. The dye-sensitized solar cell (DSSC) fabricated using this optimized polymer electrolyte achieved a high power conversion efficiency of 4.40% than the pure PVDF-HFP/KI/I2 (1.74%) at similar experimental conditions. Thus, the 2-MCBI doped polymer electrolyte has proven to be an effective substitute to the liquid electrolyte in DSSCs.