The reliability of high-performance AlInAs/GaInAs heterojunction bipolar transistors (HBTs) grown by molecular beam epitaxy (MBE) is discussed. Devices with a base Be doping level of 5*10/sup 19/ cm/sup -3/ and a base thickness of approximately 50 nm displayed no sign of Be diffusion under applied bias. Excellent stability in DC current gain, device turn-on voltage, and base-emitter junction characteristics was observed. Accelerated life-test experiments were performed under an applied constant collector current density of 7*10/sup 4/ A/cm/sup 2/ at ambient temperatures of 193, 208, and 328 degrees C. Junction temperature and device thermal resistance were determined experimentally. Degradation of the base-collector junction was used as failure criterion to project a mean time to failure in excess of 10/sup 7/ h at 125 degrees C junction temperature with an associated activation energy of 1.92 eV.>
No takes yet. Share an insight, caveat, or question.
Hafizi et al. (1993) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: