Synthesis and properties of new dialkoxyphenylene quinoxaline‐based donor‐acceptor conjugated polymers and their applications on thin film transistors and solar cells

Synthesis, properties, and optoelectronic device applications of four new bis‐[4‐(2‐ethyl‐hexyloxy)‐phenyl]quinoxaline( Qx(EHP) )‐based donor‐acceptor conjugated copolymers are reported, in which the donors are thiophene( T ), dithiophene( DT ), dioctylfluorene( FO ), and didecyloxyphenylene( OC10 ). The optical band gaps ( E g ) of PThQx(EHP) , PDTQ(EHP) , POC10DTQ(EHP) , and PFODTQ(EHP) estimated from the onset absorption are 1.57, 1.65, 1.77, and 1.92 eV, respectively. The smallest E g of PThQx(EHP) among the four copolymers is attributed to the balanced donor/acceptor ratio and backbone coplanarity, leading to a strong intramolecular charge transfer. The hole mobilities obtained from the thin film transistor (TFT) devices of PThQx(EHP) , PDTQ(EHP) , POC10DTQ(EHP) , and PFODTQ(EHP) are 2.52 × 10 −4 , 4.50 × 10 −3 , 4.72 × 10 −5 , and 9.31 × 10 −4 cm 2 V −1 s −1 , respectively, with the on‐off ratios of 2.00 × 10 4 , 1.89 × 10 3 , 4.07 × 10 3 , and 2.30 × 10 4 . Polymer solar cell based on the polymer blends of PFODTQ(EHP) , PThQx(EHP) , POC10DTQ(EHP) , and PDTQ(EHP) with [6, 6]‐phenyl C61‐butyric acid methyl ester (PCBM) under illumination of AM1.5 (100 mW cm −2 ) solar simulator exhibit power conversion efficiencies of 1.75, 0.92, 0.79, and 0.43%, respectively. The donor/acceptor strength, molecular weight, miscibility, and energy level lead to the difference on the TFT or solar cell characteristics. The present study suggests that the prepared bis[4‐(2‐ethyl‐hexyloxy)‐phenyl]quinoxaline donor‐acceptor conjugated copolymers would have promising applications on electronic device applications.