AuAl2: Optical Properties and Consideration as a Transparent Electrode Material

AuAl2 is a purple colored intermetallic compound with reasonably high metallic conductivity (σ > 105 Ω−1 cm−1). The optical properties of this material are determined by Kramers-Kronig analysis of reflectance data obtained over a range of photon energies 0.03 < hν < 11 eV. The distinctive color is associated with a reflectance minimum in the green, λ ≈ 550 nm (hν ≈ 2.2 eV). Near this wavelength, AuAl2 also exhibits a minimum in its absorption coefficient of value ≈ 3.7 × 105 cm−1 which is low for metals with comparable electrical conductivity. This material in thin film form may be of possible interest in radiation sensing devices which require electrodes with reasonable transparency in the visible spectral region. AuAl2 ist eine purpurfarbige intermetallische Verbindung mit ziemlich hoher metallischer Leitfähigkeit (σ > 105 Ω−1 cm−1). Die optischen Eigenschaften dieses Materials werden durch die Kramers-Kronig-Analyse von Reflexionsmessungen im Photonenenergie-Bereich von 0,03 < hν < 11 eV bestimmt. Die besondere Farbe ist mit einem Reflexionsminimum bei λ = 550 nm (grün) (hν ≈ 2,2 eV) verbunden. In der Nähe dieser Wellenlänge zeigt AuAl2 auch ein Minimum in seinem Absorptionskoeffizienten mit dem Wert ≈ 3,7 × 105 cm−1, welcher gering ist für Metalle mit vergleichbarer elektrischer Leitfähigkeit. Dieses Material in Dünnschichtanordnung ist möglicherweise von Interesse für Strahlungsmessungsvorrichtungen, welche Elektroden mit ausreichender Durchlässigkeit im sichtbaren Spektralgebiet benötigen.