Guiding and magneto–optical properties of TGG waveguide by proton implantation combined with femtosecond laser ablation

This is the authors' abstract. We don't add key points for this paper.

Integrating the magneto–optical effect into a waveguide-based photonic device becomes more and more interesting. In the work, the planar optical waveguide firstly was prepared in a terbium gallium garnet crystal (TGG) via the proton implantation with the energy of 4 × 10 −1 MeV and the fluence of 6 × 10 8 ions/μm 2 . Subsequently, a femtosecond laser with a central wavelength of 800 nm and a power of 3 mW was used to ablate the surface of the planar waveguide, forming the ridge optical waveguide. The dark-mode curve of the planar waveguide was measured by a prism coupling technique. The top-view morphology of the ridge waveguide was observed via a Nikon microscope. The mode field distributions of the planar and ridge waveguides were obtained by an end-face coupling system, and the propagation losses of the two waveguides were measured to be 2.26 dB/cm and 2.58 dB/cm, respectively. The Verdet constants were measured to be −72.7 °/T·cm for the TGG substrate and −60.7 °/T·cm for the ridge waveguide. The TGG waveguides have a potential in the fabrication of magneto–optical waveguide devices.