Fabrication and characterization of n-ZnO/p-AlGaN heterojunction light-emitting diodes on 6H-SiC substrates

We report on the fabrication of n-ZnO/p-AlGaN heterojunction light-emitting diodes on 6H-SiC substrates. Hydride vapor phase epitaxy was used to grow p-type AlGaN, while chemical vapor deposition was used to produce the n-type ZnO layers. Diode-like, rectifying I–V characteristics, with threshold voltage ∼3.2 V and low reverse leakage current ∼10−7 A, are observed at room temperature. Intense ultraviolet emission with a peak wavelength near 389 nm is observed when the diode is forward biased; this emission is found to be stable at temperatures up to 500 K and shown to originate from recombination within the ZnO.