The high cycle fatigue behaviour of autoclave-cured carbon fibre-reinforced polymer (CFRP) composite gears is investigated. The CFRP gears were milled from a composite plate and tested in mesh with a steel drive gear under five torque loads ranging between 0.4 and 0.8 Nm in unlubricated conditions. A detailed gear damage analysis is conducted by employing scanning electron microscopy and high-resolution optical microscopy. Epoxy matrix microcracking is found to be the damage mechanism that leads to the final delamination failure. CFRP gears exhibited a significantly improved performance and a longer fatigue lifespan in comparison with the polymer and polymer composite gears.