Preparation of antimicrobial polycaprolactone‐silica composite films with nanosilver rods and triclosan using roll‐milling method

In this study, antimicrobial polycaprolactone composite films containing 12.5% silica and 0.15% silver nanorods were prepared using the roll‐milling method. The destruction of E. coli and S. aureus on the surface of the composite films was evaluated after 6 hr of incubation at 37°C. For the E. Coli , no bacterial contamination was detected after 6 hr and the film surface was completely disinfected with 100% reduction of the microbial contamination. For the S. aureus , 94% reduction of the bacterial contamination was observed after 6 hr. The results were compared with the composite films containing triclosan, a broad‐spectrum antimicrobial agent. The antimicrobial activity tests with 0.25% triclosan incorporated polycaprolactone‐silica composite films showed only 70% reduction of E. coli and 95% reduction of S. aureus after 6 hr. The results demonstrated that the use of silver nanoparticles in the biopolymer industry has huge potential for the self‐cleaning applications.