Fabrication of surface‐enhanced Raman scattering‐active ZnO/Ag composite microspheres

We show in this paper how zinc oxide (ZnO)/silver (Ag) composite microspheres can be prepared by the reduction of Ag(NH 3 ) 2 + with the reducing agent formaldehyde in aqueous solution on the surface of ZnO microspheres. During the preparation, Sn 2+ was absorbed on the surface of ZnO microspheres for sensitization and activation, and then Ag(NH 3 ) 2 + was reduced to Ag nanoparticles by the reducing agent to obtain ZnO/Ag composite microspheres. SEM and TEM images revealed silver nanoparticles with a diameter ranging from tens to 100 nm. X‐Ray photoelectron spectra (XPS), X‐ray diffraction (XRD) patterns and UV‐vis spectra were used to characterize the structure of the ZnO/Ag composite microspheres. The origin of the surface‐enhanced Raman scattering properties was traced to the surface of the ZnO/Ag composite microspheres. The enhancement factor was estimated in detail, and the enhancement mechanism for the SERS effect was also investigated.