Electrochemical Stability of Li6.5La3Zr1.5M0.5O12 (M = Nb or Ta) against Metallic Lithium

The electrochemical stability of Li6.5La3Zr1.5Nb0.5O12 (LLZNO) and Li6.5La3Zr1.5Ta0.5O12 (LLZTO) against metallic Li was studied using direct current (DC) and electrochemical impedance spectroscopy (EIS). Dense polycrystalline LLZNO (ρ=97 %) and LLZTO (ρ=92 %) were made using sol-gel synthesis and rapid induction hot-pressing at 1100 °C and 15.8 MPa. During DC cycling tests at room temperature (±0.01 mA/cm2 for 36 cycles), LLZNO exhibited an increase in Li-LLZNO interface resistance and eventually short-circuiting while the LLZTO was stable. After DC cycling, LLZNO appeared severely discolored while the LLZTO did not change in appearance. We believe the increase in Li-LLZNO interfacial resistance and discoloration are due to reduction of Nb5+ to Nb4+. The negligible change in interfacial resistance and no color change in LLZTO suggest that Ta5+ may be more stable against reduction than Nb5+ in cubic garnet versus Li during cycling.