The first fabrication of 3-in-diameter, thin films of thallium-based superconductors is reported. (Tl/sub 0.5/Pb/sub 0.5/)Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub 9/ thin films on LaAlO/sub 3/ are found to display the best surface resistance (R/sub s/) properties of any superconductor at higher temperatures and show approximately 50* better performance than copper at 100 K and 10 GHz. A Tl/sub 2/Ba/sub 2/CaCu/sub 2/O/sub 8/ thin film, processed as a 1.8-m-long, 10- mu m-wide meander line carries about 1*10/sup 7/ A/cm/sup 2/ at 4.2 K and 2*10/sup 6/ A/cm/sup 2/ at 80 K. The thallium-based superconductors are compared to YBa/sub 2/Cu/sub 3/O/sub 7/ with respect to T/sub c/, R/sub s/, and Q.>