Photoinitiated surface grafting of synthetic fibers, I. Photoinitiated surface grafting of ultra high strength polyethylene fibers

Photoinitiated surface grafting of acrylic monomers has been carried out onto high strength polyethylene (HSPE) yarn by means of a continuous process. The grafting reaction is initiated by UV irradiation of the yarn after presoaking in an acetone solution of initiator and monomer. Four initiators, benzophenone (BP), 4‐chlorobenzophenone (4‐CBP), 2‐hydroxy‐2‐cyclohexylacetophenone (HHA), and 2,2‐dimethoxy‐2‐phenylacetophenone (DMPA), and two monomers, acrylic acid (AA) and acrylamide (AM), have been used. After short irradiation time (10 to 20 s) successful grafting is obtained, as shown by ESCA and IR‐ATR spectra, dye adsorpotion from aqueous solution, and measurements of adhesion of single filaments to epoxy resin. Grafting efficiency of 74% has been reached for AA as monomer (26% is homopolymer). The tensile strength and modulus of the HSPE yarn are retained in the grafting process. The degree of surface grafting is mainly a function of structure and concentration of monomer and photoinitiator in the presoaking solution and of the irradiation conditions used. Increasing irradiation time gives increasing amounts of grafted polymer up to a certain limiting value. The reactivities of the four initiators have been compared showing the highest grafting yields of AA with BP and of AM with 4‐CBP as photoinitiator. AA grafted HSPE yarn can be dyed to rather deep color by dipping in an aqueous solution of Crystal Violet. Increased dye absorption by a factor of up to seven has been measured for yarn grafted with AA to the maximum level obtained. The filaments of the grafted yarn show increased adhesion to epoxy resin by a factor of up to five compared with the ungrafted filaments.