Yttria-stabilized zirconia (YSZ) thin films were deposited by reactive magnetron sputter deposition from a composite Zr–Y target in Ar–O2 mixtures. Hysteresis was observed as a function of oxygen flow rate f. For a discharge current of 0.4 A and a total pressure P of 5 mTorr, for example, the target oxidized at f>2.3 ml/min, with the reverse transition from an oxidized to a metallic target surface occurring at 1.95 ml/min. The deposition rate was 2.7 μm/h in the metallic mode and 0.1 μm/h in the oxide mode. Fully oxidized (Y2O3)0.1(ZrO2)0.9 was obtained for f>2.0 ml/min, even in the metallic mode. While films deposited with P=3–20 mTorr were continuous, for P>20 mTorr crazing was apparent as expected for a ceramic film in a tensile stress state. For P<3 mTorr, the films delaminated due to excessive compressive stress. X-ray diffraction and electron microscopy results showed that the films were polycrystalline cubic YSZ with a columnar structure and an average grain diameter of 15 nm. Fully dense films were obtained at a deposition temperature of 350 °C. Temperature-dependent impedance spectroscopy analysis of YSZ films with Ag electrodes showed that the oxygen ion conductivity was as expected for YSZ.
No takes yet. Share an insight, caveat, or question.
Thiele et al. (1991) studied this question.