Dynamic crystallization of polypropylene and wood‐based composites

Thermoplastic composites made of an isotactic polypropylene (iPP) matrix and woodflour (WF) were prepared by melt‐blending, using twin‐screw extrusion and injection molding. Up to 20 wt % of the composite was composed of WF. The incorporation of an interfacial agent made of an ethylene/methacrylic acid copolymer to iPP and WF, PP/WF, binary blends causes a compatibilization effect that becomes evident due to a reduction in the crystallization temperature of PP. In both the binary composites and the compatibilized or ternary composites, the PP adopts an α or monoclinic structure when crystallization occurs from the melt under dynamic conditions at cooling rates between 1 and 20°C min−1. On the other hand, X‐ray diffraction analysis using synchrotron radiation of the injection‐molded samples demonstrates the existence of a β or trigonal form in the binary as well as the ternary PP/WF composites. They reach kβ levels between 0.18 and 0.25, which can be interpreted as the co‐operation between a reduction of the crystallization rate and the shear effect induced during the injection.